390ml 3:1 High Tensile Strength Chemcial Anchor Adhesive For Thread
Rods
Chemical anchor adhesive, epoxy injection mortar, Chemical fixing
glue,
Chemical anchoring system used for anchoring and rebar connections
in concrete.
Item #: FixingChor139
Capacity: 390ml
Materials: Epoxy
Mixing Ratio: 3:1
Product Description:
390ml 3:1 High Tensile Strength Chemcial Anchor Adhesive For Thread
Rods is
a high performance, two components pure epoxy resin system. strong
fixing with exceptionally
high chemcial resistance.Applied in one single action this resin
will produce a high performance,
Characteristics
Used for studs and relatively small diameter rebar. ⋅
Fixings in concrete, wood, or other high strength materials.
Suitable for medium loads and non-critical applications.
Fast working times for early loading in time sensitive
applications.
Use in extremely cold environments and fixings holes.
Good durability formulation, resistance to chemicals.
Application Range
Fixing of the following substrates:
Concrete
Hard natural and reconstituted stone
Solid rock and masonry
Metal Work, carpentry
Fixing of handrails, balustrades and supports
Fixing of railings
Fixing of window and door frames
Mechanical and electrical services installation
Anchoring of supports for ducting and equipment.
For structural work:
Rebar / steel reinforcement anchoring in new and refurbishment
works.
Threaded rods
Bolts and special fastening systems
Testing project | Condition | Index |
Gel Performance (According to China National Standard GB50728-2011) |
Splitting Tensile Strength (MPa) | Under (23±2)℃,(50±5)%RH, tested by loading speed of 2mm/min | ≥8.5 |
Flexural Strength (MPa) | ≥50 (no fragment damage) |
Compressive Strength (MPa) | ≥60 |
Bonding Capacity (According to China National Standard GB50728-2011) |
Steel-Steel Tensile Shear Strength (MPa) | (23±2)℃,(50±5)%RH | ≥10 |
Bonding strength of Ribbed steel bar (or screw) with concrete under
constrain drawing condition | (23±2)℃ (50±5)%RH | C30,Ф25,L=150mm | ≥11 |
C60,Ф25,L=150mm | ≥17 |
Steel-Steel T-peeling strength (mm) | (23±2)℃,(50±5)%RH | ≤25 |
Non-volatile content | (105±2)℃,(180±5)min | ≥99% |
Ageing resistance to heat and humidity 90d |
Reduction rate of tensile strength | Under normal room temperature | ≤12% |
(According to China National Standard JGJ145-2013) |
Tensile Strength (after high temperature welding) | Dia12 Grade II steel, C30 concrete Hole dia.16mm, Depth: 150mm | 55.1N, 57.0N, 54.8N |
High bonding strength,
Can be applied in severe environment
With molecular structure combining the Hydrophilic group and
hydrophobic group
Can operate and keep high performance in environment of moisture,
hot and still
works even if the surface of hole is smooth.
Non-cracked concrete
Can use in damp area
High load capacity
Non-sag, even overhead
Styrene-free
Low odour
Non contraction after harden
High stability
No transportation restrictions
Good elongation property
No breaking under high stressing.
repristinate after stressing.
ATTENTION
- Do not install anchors when the temperature is less than 10°C.
- If the cartridge is not finished, please clean the opening, then
put the plug back and cap tightly.
- At temperatures below 10°C should be warmed or stored in
temperatures
of 10-30°C for 24hours prior to use to improve product flow and
cure.
- If the gelling time expires, please use a new static mixer.
- Do not cut or shorten nozzles.
- It can be used again in the future by replacing the static mixer.
- Please ensure hole is properly cleaned. Hole may be damp but must
be free from water.
- Do not install anchors when substrate temperature is less than
0°C.
r.