390ml 3:1 Modified Pure Epoxy Chemcial Anchor Adhesive For
Structural Strengthening
Chemical anchor adhesive, epoxy injection mortar, Chemical fixing
glue,
Chemical anchoring system used for anchoring and rebar connections
in concrete.
Item #: FixingChor110
Capacity: 1000ml
Materials: Epoxy
Mixing Ratio: 3:1
Product Description:
390ml 3:1 Modified Pure Epoxy Chemcial Anchor Adhesive For
Structural Strengthening is
a two component, high tensile strength, modified pure epoxy
chemcial anchor adhesive.
strong fixing system with exceptionally high chemcial
resistance.Applied in one single action
this resin will produce a high performance,
Suitable for
Non-cracked concrete
Reinforcement bars
For fixing of:
Consoles
High-racks
Machines
Staircases
Wooden constructions
Reinforcement bars
Steel constructions
Pass GB50728-2011
Humidity resistance testing
Freeze-thaw resistance Testing
Resistance to fatigue stress Testing
Resistance of long term stress testing etc .
Can be used in projects with Design Period of 50 years.
Testing Items | Condition | Index |
Adhesive Performance (According to China National Standard GB50728-2011) |
Splitting Tensile Strength (MPa) | Under (23±2)℃,(50±5)%RH, tested by loading speed of 2mm/min | ≥8.5 |
Flexural Strength (MPa) | ≥50 (no fragment damage) |
Compressive Strength (MPa) | ≥60 |
Bonding Capacity (According to China National Standard GB50728-2011) |
Steel-Steel Tensile Shear Strength (MPa) | (23±2)℃,(50±5)%RH | ≥10 |
Bonding strength of Ribbed steel bar (or screw) with concrete under
constrain drawing condition | (23±2)℃ (50±5)%RH | C30,Ф25,L=150mm | ≥11 |
C60,Ф25,L=150mm | ≥17 |
Steel-Steel T-peeling strength (mm) | (23±2)℃,(50±5)%RH | ≤25 |
Non-volatile content | (105±2)℃,(180±5)min | ≥99% |
Ageing resistance to heat and humidity 90d |
Reduction rate of tensile strength | Under normal room temperature | ≤12% |
(According to China National Standard JGJ145-2013) |
Tensile Strength (after high temperature welding) | Dia12 Grade II steel, C30 concrete Hole dia.16mm, Depth: 150mm | 55.1N, 57.0N, 54.8N |
High bonding strength,
Can be applied in severe environment
With molecular structure combining the Hydrophilic group and
hydrophobic group
Can operate and keep high performance in environment of moisture,
hot and still
works even if the surface of hole is smooth.
Good elongation property
No breaking under high stressing.
repristinate after stressing.
Our Product Lines:
- Carbon Fiber Reinforcement System:
XQ-CFC 300gsm, 200gsm fabric and adhesives XQ-XW
- Steel Bonding System:
XQ-GZ Epoxy grouting adhesives,
XQ-JGN Plate bonding Adhesives
- Crack Repairing System:
XQ-GF Crack grouting adhesives,
XQ-FF crack seal adhesives
- Chemical Anchoring
390ml(3:1), 585ml(3:1), 650ml(1:1),